| CHEMICAL RESISTANCE DATA INFORMATION | ||||||||
| Chemical | Concentration |
Nylon 6 |
Nylon 66 |
Nylon 612 |
PET / PBT |
PP |
||
| Acetic Acid | 100% |
Poor |
Poor |
Poor |
Fair |
Fair |
||
| Acetone | 100% |
Good |
Good |
Good |
Good |
Good |
||
| Ammonia Liquid | Good |
Good |
Good |
No |
Good |
|||
| Aniline | 100% |
Poor |
Poor |
Poor |
Good |
Poor |
||
| Benzene | 100% |
Good |
Good |
Good |
Good |
No |
||
| Bleaching Solutions | Dilute |
No |
No |
No |
Good |
Good |
||
| Caustic Potash | 10% |
Good |
Good |
Good |
Good |
Good |
||
| Caustic Potash Con. | 50% |
Good |
Good |
Good |
Poor |
Good |
||
| Chlorine Water | Saturated |
No |
Poor |
No |
No |
Fair |
||
| Chloroform | 100% |
No |
No |
No |
Good |
No |
||
| Chromic Acid | 10% |
Poor |
Poor |
Poor |
Good |
Good |
||
| Citric Acid | 10% |
Poor |
Poor |
Poor |
Good |
Good |
||
| Detergent Soaps | Good |
Good |
Good |
Good |
Good |
|||
| Ethanol | 96% |
Poor |
Good |
Poor |
Good |
Good |
||
| Ethylacelate | 100% |
Good |
Good |
Good |
Good |
Good |
||
| Formic Acid | 98% |
No |
No |
No |
No |
No |
||
| Fuel Oil | Good |
Good |
Good |
Good |
Poor |
|||
| Glycerin | Good |
Good |
Good |
Good |
Good |
|||
| Hydrochloric Acid | 30% |
No |
No |
No |
Poor |
Good |
||
| Lactic Acid | 20% |
Poor |
Poor |
Poor |
Good |
Good |
||
| Methyl Alcohol | 100% |
Good |
Good |
Good |
Good |
Good |
||
| Mineral Oil | Good |
Good |
Good |
Good |
Good |
|||
| Nitric Acid | 10% |
No |
No |
No |
Good |
Good |
||
| Nitric Acid | 50% |
No |
No |
No |
Good |
Poor |
||
| Oleic Acid | 100% |
Good |
Good |
Good |
Good |
Good |
||
| Oxalic Acid | 10% |
No |
No |
Fair |
Good |
Fair |
||
| Petrol | Good |
Good |
Good |
Good |
No |
|||
| Phosphoric Acid | 85% |
No |
No |
No |
Good |
Good |
||
| Sea Water | Good |
Good |
Good |
Good |
Good |
|||
| Sodium Chloride (salt) | Good |
Good |
Good |
Good |
Good |
|||
| Sodium Hydroxide | 10% |
Good |
Good |
Good |
No |
Good |
||
| Sodium Hydroxide | 50% |
Good |
Good |
Good |
No |
Good |
||
| hodium Hypochloride | 10% |
No |
No |
No |
Good |
Good |
||
| Stearic Acid | 100% |
Poor |
Poor |
Poor |
Good |
Good |
||
| Sulfuric Acid | 10% |
No |
No |
No |
Good |
Good |
||
| Sulfuric Acid | 100% |
No |
No |
No |
No |
No |
||
| Ttrachloroethylene | Good |
Good |
Poor |
No |
No |
|||
| Tuluene | 100% |
Good |
Good |
Good |
Good |
No |
||
| Trichloroethylene | Good |
Good |
Poor |
No |
No |
|||
| Turpentine | 100% |
Good |
Good |
Good |
Good |
No |
||
| Vaseline | Good |
Good |
Good |
Good |
Good |
|||
| Vegetable Oil | Good |
Good |
Good |
Good |
Good |
|||
| The above information is given on the assumption that the temperature of the chemical does not exceed 20 °C. | ||||||||
| PROPERTIES OF MONOFILAMENTS | ||||||||
Unit |
Nylon 6 |
Nylon 66 |
Nylon 612 |
PET / PBT |
PP |
|||
| Specific weight | g/cm3 |
1,14 |
1,14 |
1,06 |
1,34 |
0,91 |
||
| Melting Point | °C |
220 |
255 |
212 |
255 |
168 |
||
| Maximum working temperature | °C |
100-120 |
100-120 |
100-120 |
120 |
70 |
||
| Moisture absorption | % |
3 |
2,8 |
0,25 |
0,3 |
0.00 |
||
| Water absorption | % |
9,5 |
8,5 |
3 |
0,5 |
0,01 |
||
| Tensile strength dry | N/mm2 |
80 |
8,5 |
61 |
55 |
36 |
||
| Loss of stiffness (wet) | % |
70/80 |
50/60 |
30/40 |
1,2 |
1,2 |
||
| Abrasion resistance | Good |
Good |
Good |
Fair |
Good |
|||
| Bend recovery | Good |
Good |
Good |
Fair |
Fair |
|||
| Toxicity | none |
none |
none |
none |
none |
|||
| Swelling in water | % |
2 |
2 |
2 |
0 |
0 |
||
| The information in both the above tables is based on our general experience and is given in good faith. | ||||||||
| We are unable to accept responsability in respect of factors that are outside of our knowledge or control, | ||||||||
| and affect the use of the products. No warranty is given or is implied with respect to such information. | ||||||||